Our Gloss Metallic vinyl wrap has a smooth, high-gloss finish and is crafted from the high-grade polymeric multilayered calendared vinyl film, complete with air release channels. Gloss Metallic wrap is durable and has good conformability; it’s stretchable enough to wrap around every edge and recessed area of your vehicle with ease. Gloss Metallic also uses a safe solvent polyacrylate adhesive, which is easy to install and gentle on car paint. Conformable polymeric material with stable color pigments. Suitable for full car wrapping (or any other smooth or curved surface).

18m roll.

The thickness of the film: 0.16mm
The thickness of film with release liner: 0.32mm
Type of film: High grade polymeric multilayered calendared vinyl film with air release channels

Width & Length: Standard roll size - 1.52m*18m (59.8"* 708,6", 4.98ft*59ft, 1.66yd* 19,6yd)

Series: 190 series

Adhesive: Solvent polyacrylate

Adhesive performance properties: (1mil adhesive on 1mil material, bonded to stainless steel panel)

180°Peel (PSTC-101), 20 minute bond – 2.2 lb/inch, 24 hour bond – 3.5 lb/inch

Release liner: Kraft white silicone-coated, paper with a double-sided polyethylene coating

Storing period (shelf life): 2 years if stored in +10°C to +20°C, relative humidity 50%, in original package, away from direct sunlight, clean and dry place

Avg. indoor life: 4 years when followed rules of application and usage

Avg. outdoor life: 3 years when followed rules of application and use

Application: from +17°C to +25°C, usage from -55°C to +65°C

Dimensional stability: shrinkage less than 4%

Plastification: between 27%-35%

Breaking Strength: 22.7 N/10mm (Average) Test Method: ASTM D3759/D3759M-057.4 N/10mm (Average)

Light Ageing in UV Exposure: Test Method: ASTM D4329-13 Cycle A & ISO 105-A02:1993/Cor.2:2005,

Test result: 5

Exposure cycle: ASTM D4329-13 cycle A,

Lamp type: UVA-3408h UV at (60±2.5)°C BPT, 0.89 W/ (m2•nm)@340nm, 4h condensation at (50±2.5)°C BPT, Exposure duration: 49h

Recommended application tools: Squeegee, buffer, knife, masking tape, heat gun, magnets, gloves, IRR thermometer, IRR heater

Application method: Standard methods for calendered films. No overstretching. Post heating

Post-heating temperature: 110°C flat surfaces, 130°C curves, and overlaps

Cure time: 24 hours above 10°C

Aftercare: PH neutral, Avoid wax or solvents

Directional: No

Tools: soft squeegees with buffers